导电胶AR-P-5090 和 AR-P-5091

点击查看大图

价格：￥电议

型号：原产地：中国大陆发布时间：2022/1/21 17:07:55更新时间：2024/11/12 6:24:44

产品摘要：德国ALLRESIST防护涂层PMMAElectra92(AR-PC5090)，用于非氮基电子束电阻的导电保护涂层，用于在绝缘衬底上耗散电子束电荷的顶层。

产品完善度：访问次数：180

企业档案

会员类型：初级版会员

已获得易推广信誉等级评定

8成长值

(0 -40)基础信誉积累，可浏览访问

(41-90)良好信誉积累，可接洽商谈

(91+ )优质信誉积累，可持续信赖

易推广初级版会员：3年

工商认证【已认证】

最后认证时间：

注册号：【已认证】

法人代表：【已认证】

企业类型：经销商【已认证】

注册资金：人民币100万【已认证】

产品数：480

参观次数：261902

手机网站：http://m.yituig.com/c162928/

商铺地址：http://www.szkesda.com

产品分类

详细内容

Protective Coating PMMA Electra 92 （AR-PC 5090）

Conductive protective coating for non-novolak-based e-beam resists

Top layer for the dissipation of e-beam charges on insulating substrates

Characterisation 描述

- as protective coating, this resist is not sensitive to light / radiation

- thin, conductive layers for the dissipation of charges during electron exposure

- coating of non-novolac PMMA, CSAR 62, HSQ et al.

- longterm-stable ａnd cost-efficient alternative to Espacer

- easy removal with water after exposure

- polyaniline-derivative dissolved in water ａnd IPA

Conductivity 导电率

Resistance measurements of AR-PC 5090.02 layers obtained after spin deposition. For thinner films, the resistance increases ａnd the conductivity decreases.

Process parameters 工艺参数

REM dissipation of charges

200 nm-squares written on quartz without distortion caused by charges with AR-P 662.04 ａnd AR-PC 5090.02

Protective Coating PMMA Electra 92 （AR-PC 5090）

Process conditions

This diagram shows exemplary process steps for resist Electra 92 - AR-PC 5090.02 ａnd PMMA-resist AR-P 664.04.

All specifications are guideline values which have to be adapted to own specific conditions.

Processing instructions

The conductivity may be varied by adjusting the thickness with different rotational speeds. Thicker layers of 90 nm thus have a 2.5 times higher conductivity as compared to 60 nm thick layers.

For the build-up of an even conductive layer, the substrate should be wetted with the resist solution before the spin process is started.

Protective Coating Novolac Electra 92 （AR-PC 5091）

Conductive protective coating for novolac-based e-beam resists

Top layer for the dissipation of e-beam charges on insulating substrates

Characterisation

- as protective coating, this resist is not sensitive to light / radiation

- thin, conductive layers for the dissipation of charges during electron exposure

- coating of novolac-based e-beam resist AR-N 7000

- longterm-stable ａnd cost-efficient alternative to Espacer

- easy removal with water after exposure

- polyaniline-derivative dissolved in water ａnd IPA

Conductivity

Resistance measurements of AR-PC 5091.02 layers obtained after spin deposition. For thinner films, the resistance increases ａnd the conductivity decreases.

Note: Novolac-based e-beam resists possess other surface properties than CSAR 62 or PMMA. AR-PC5091 was thus developed with a different solvent mixture. In all other respects however, the polymer composition of AR-PC 5090 ａnd AR-PC 5091 is identical so that both resists are referred to as “Electra 92“.

Process parameters

REM dissipation of charges

50 nm lines written on glass at a pitch of 150 nm with AR-N 7520.07 ａnd AR-PC 5091.02

Protective Coating Novolac Electra 92 （AR-PC 5091）

Process conditions

This diagram shows exemplary process steps for resist Electra 92 （AR-PC 5091.02）ａnd e-beam resist AR-N 7520.07neu. All specifications are guideline values which have to be adapted to own specific conditions.

Processing instructions

The conductivity may be varied by adjusting the thickness with different rotational speeds. Thicker layers of 90 nm thus have a 2.5 times higher conductivity as compared to 60 nm thick layers. In the case that crack formation is observed after tempering of the protective coating, the tempering step can be omitted.

For the build-up of an even conductive layer, the substrate should be wetted with the resist solution before the

spin process is started.

Protective Coating Electra 92

Application examples for PMMA-Electra 92

Shelf live of Electra 92

Conductivity properties of differently aged Electra 92 batches

The conductivity was determined as a function of the measured temperature. At temperatures < 100 °C, both resists show a virtually identical conductivity. Electra 92 is thus characterised by a very long shelf life. Conductivity measurements up to a temperature of 160°C which were performed directly on a hotplate showed a large increase of the conductivity by a factor of 10 （see diagram）. This fact is due to the complete removal of water from the layer. After a few hours of air humidity absorption under room conditions, the conductivity decreases again to

the initial value. In the high vacuum of e-beam devices, the water is also completely removed ａnd the conductivity thus increases accordingly. This effect has been demonstrated in direct conductivity measurements under mediate vacuum conditions. Temperatures above 165 °C destroy the polyaniline irreversibly ａnd no conductivity is observed any more

CSAR 62 on glass with Electra 92 for deriving

30 – 150 nm squares of CSAR 62 on glass

The combination of CSAR 62 with Electra 92 - AR-PC5090.02 offers the best options to realise complex ebeam structuring processes on glass or semi-insulating substrates like e.g. gallium arsenide. The excellent sensitivity ａnd highest resolution of the CSAR are complemented harmoniously by the conductivity of Electra 92.

CSAR 62 ａnd Electra 92 on glass

At a CSAR 62 film thickness of 200 nm, squares with an edge length of 30 nm could reliably be resolved on glass.

PMMA Lift-off on glass with Electra 92

200 nm squares produced with 2-layer PMMA lift-off

Initially, the PMMA resist AR-P 669.04 （200 nm thickness） was coated on a quartz substrate ａnd tempered. The se cond PMMA resist AR-P 679.03 was then applied （150nm thickness）ａnd tempered, followed by coating with Electra 92. After exposure, Electra 92 was removed with

water, the PMMA structures were developed （AR 600-56）ａnd the substrate vaporised with titanium/gold. After a liftoff with acetone, the desired squares remained on the glass with high precision.

PMMA-Lift-off auf Glas mit Electra 92

Protective Coating Electra 92

Application examples for PMMA Electra 92

Electra 92 with HSQ on quartz

20 nm bars of HSQ, prepared on quartz AR-PC 5090.02

After a coating of Electra 92 on an HSQ resist, even this resist can be patterned on a quartz substrate with very high quality. The HSQ resist （20 nm thickness） was irradiated with the required area dose of 4300 ?C/cm?.

SX AR-PC 5000/90.2 was subsequently completely removed within 2 minutes with warm water ａnd no residues could be detected. After development of the HSQ resist, the structures with high-precision 20 nm bars remained.

Lift-off struktures on garnet

Lift-off structures on garnet （University of California, Riverside,Department of Physics ａnd Astronomy）

Plasmonic structures on quartz

Silver nanoparticles on quartz, generated with AR-P 672.11 ａnd ARPC 5090.02 （Aarhus University, Denmark）

Application examples for Novolac Electra 92