标题C63020镍铝青铜回火

提供者：东莞市协昌金属材料有限公司发布时间：2021/10/28 阅读次数：270次 >>进入该公司展台

典型用途

航空航天：衬套、轴承
工业：轴承、滚动轴承成型模具、土方设备液压衬套、阀球、阀门零件（低温）

Similar or Equivalent Specification

CDA	ASTM	SAE	AMS	Federal	Military	Other
C63020	B150 B150M		4590

Cu%	Pb%	Sn%	Zn%	Fe%	Ni%1	Al%	Co%	Cr%	Mn%	Si%
Chemical Composition according to ASTM 4590 1Ni value includes Co. Note: Cu + Sum of Named Elements, 99.5% min. Single values represent maximums.
Rem.	0.03	0.25	0.30	4.00- 5.50	4.20- 6.00	10.00- 11.00	0.20	0.05	1.50	0.15

Copper Alloy UNS No.	Machinability Rating	Density (lb/in3 at 68 °F)	Density (gm/in3 at 20 °C)
C63020		0.275	7.6

Mechanical Properties according AMS 4590

Tensile Strength, min		Yield Strength, at 0.2% Offset, min		Elongation, in 2 inches (50.8 mm) or 4D, min, min	Rockwell "C" Hardness	Remarks
ksi	MPa	ksi	MPa	%	min HRC
135	931	100	689	6	26

	US Customary	Metric
Melting Point - Liquidus	1940° to 1967 °F	1060° to 1075 °C
Density	0.274 lb/in3 at 68 °F	7.6 gm/cm3 at 20 °C
Specific Gravity	7.6	7.6
Electrical Resistivity	132.33 ohms-cmil/ft at 68 °F	22.0 microhm-cm at 20 °C
Thermal Conductivity	31.2 Btu/sq ft/ft hr/°F at 68 °F	54.0 W/m at 20 °C
Coefficient of Thermal Expansion 68-572	9.4 · 10-6 per °F (68-572 °F)	17.0 · 10-6 per °C (20-300 °C)