当前位置：易推广 > 其他产品/服务 > 其他产品/服务 > 其他产品/服务 > 深圳市深鹏孚润滑油有限公司 > 产品展示 > 福斯润滑油 > FUCHS RENOLIN B68 HVI

FUCHS RENOLIN B68 HVI

点击查看大图

价格：￥电议

型号：原产地：中国大陆发布时间：2018/4/2 14:39:31更新时间：2024/8/6 11:51:06

产品摘要：FUCHS RENOLIN B68 HVI FUCHS RENOLIN B HVI液压油　详细说明　（浏览702次）RENOLIN B HVI PrintHigh Performance, High Viscosity index HV Hydraulic OilsDiagram High Perform

产品完善度：访问次数：205

企业档案

会员类型：初级版会员

已获得易推广信誉等级评定

18成长值

(0 -40)基础信誉积累，可浏览访问

(41-90)良好信誉积累，可接洽商谈

(91+ )优质信誉积累，可持续信赖

易推广初级版会员：9年

工商认证【已认证】

最后认证时间：

注册号：【已认证】

法人代表：【已认证】

企业类型：经销商【已认证】

注册资金：人民币888万【已认证】

产品数：10016

参观次数：2228350

手机网站：http://m.yituig.com/c132299/

商铺地址：http://

产品分类

详细内容

FUCHS RENOLIN B68 HVI

FUCHS RENOLIN B HVI液压油　详细说明　（浏览702次）

RENOLIN B HVI

High Performance, High Viscosity index HV Hydraulic Oils

Diagram

High Performance, High Viscosity index HV Hydraulic Oils

The function of hydraulic oil pumps can often be improved irrespective of the machinery driven because they are isolated from the variables found at the workplace. A major factor in the performance of hydraulic system is the fluid medium. This absorbs a relatively large amount of energy when the pump is started-up because of the high internal resistance of hydraulic oil. Excessive friction also occurs if the oil＇s viscosity is too low ａnd this leads to wear. Such conditions can cause breakdowns. FUCHS has developed a series of so-called "low friction" oils which reduce energy consumption ａnd wear when hydraulic pumps are started-up. These products also improve reliability ａnd eliminate breakdowns caused by insufficient or excess viscosity, both problems associated with normal HM hydraulic oils.

The RENOLIN B HVI series of oils offer the following advantages:

Excellent viscosity-temperature behaviour
Good EP properties ａnd thus protection against wear
Excellent shear stability
Excellent oxidation stability ａnd resistance to ageing
Excellent corrosion protection
Rapid air release ａnd low foaming
Good demulsification characteristics
Good elastomer compatibility

Application:

The RENOLIN B HVI series of oils are not just high grade hydraulic oils but also excellent lubricating oils which can be used for numerous applications.

They are particularly suitable for use in hydraulic equipment operating over a wide temperature range. This means for applications requiring a low start-up viscosity but also a stable protecting lubricating film at high operating temperatures. RENOLIN B HVI series of oils contribute to a rationalization by reducing the variety of hydraulic oils in use.

RENOLIN		B 15 HVI	B 32 HVI	B 46 HVI
Hydraulic oil type
acc. to ISO 6743-4¹		HV 15	HV 32	HV 46
acc. to DIN 51 502¹		HVLP 15	HVLP 32	HVLP 46
Characteristics	Unit				Test method
Colour		0.5	1	1	ASTM D 1500
Kinematic viscosity
at 40 °C	mm²/s	15	32	46	ASTM D 445
at 100 °C	mm²/s	3.8	6.8	8.9	ASTM D 445
Viscosity index		153	180	180	ASTM D 2270
Density at 15 °C	kg/l	0.855	0.876	0.87	ASTM D 1298
Flash point, Cleveland open cup	°C	180	178	178	ASTM D 92
Pour point	°C	- 36	- 42	- 33	ASTM D 97
Neutralization number	mg KOH/g	0.3	0.3	0.3	ASTM D 974
Saponification number	mg KOH/g	0.6	0.6	0.6	ASTM D 94
Oxide ash	% mass	0.1	0.1	0.1	ASTM D 482
Water content	% mass	not traceable	not traceable	not traceable	ASTM D 95
Insolubles	% mass	not traceable	not traceable	not traceable	DIN 51 592
Demulsification	min	15	15	18	DIN 51 599
Air release at 50 °C	min	1	2	3	ASTM D 3427
Foaming,
seq. I	ml	10/0	20/0	40/0	ASTM D 892 seq. I-III
seq. II	ml	30/0	20/0	20/0	ASTM D 892 seq. I-III
seq. III	ml	10/0	60/0	50/0	ASTM D 892 seq. I-III
Copper corrosion	degree of corr.	1a-100A24	1a-100A24	1a-100A24	ASTM D 130
Rust prevention		pass A	pass A	pass A	ASTM D 665
Shear stability after 250 cycles, viscosity decrease at 100 °C	%	2	5	7	IP 294
Ageing behaviour, increase in neutralization number after 1000 h	mg KOH/g	< 2	< 2	< 2	ASTM D 943
FZG mechanical gear rig test	load stage	12	12	12	DIN 51 354-2
Vickers vane pump test, loss of mass
on ring	mg	< 120	< 120	< 120	IP 281
on vanes after 250 h	mg	< 30	< 30	< 30	IP 281
Effect on SRE-NBR 1 seal material acc. to DIN 53 538-1 at 100 °C +/– 1 °C after 7 days +/– 2 hours,
relative volume change	%	15	11	0	DIN 53 521 together with DIN 53 505
change in Shore A hardness	Shore	– 5	– 5	– 5	DIN 53 521 together with DIN 53 505