Heat-curing MoS2 solid film lubricant

Performance Features

• temperature range: -180 / +300 °C
• forms a dry, solid film lubricant
• is resistant to solvents ａnd mineral oils as well as synthetic fluids
• supports oil or grease lubrication
• provides clean assembly conditions
• is resistant to extremely high pressures
• offers corrosion protection
• improves running-in properties of oil or grease-lubricated parts substantially

Description

GLEITMO SFL 9540 is a selected combination of solid lubricants, organic binders ａnd solvents. Upon curing, GLEITMO SFL 9540 forms a dry, solid film lubricant firmly adhering, resistant to oil, to solvents ａnd to high pressures, with corrosion protection, applicable over a wide range of temperatures. In the area of boundary ａnd mixed friction, GLEITMO SFL 9540 supports an oil or grease lubrication outstandingly well.

Field of application

GLEITMO SFL 9540 improves running in conditions, protection against surface damage ａnd wear especially at high pressures ａnd low sliding speeds. In many cases, lifetime lubrication is possible. Typical Applications: Gear wheels, bearing bushes, pivot pins, plain bearing axles, special steel fitting components, chain parts, wearing rings ａnd locking disks, large threaded connections, ceramic parts, slid-ing parts exposed to high temperatures.

Method of application

The parts to be coated should be thoroughly de-greased. The surface should be dry for application of GLEITMO SFL 9540. To increase the adhesive strength, ａnd therefore the lifetime, pre-treatment of the surfaces is recommended by phosphatising or sand-blasting. In order to achieve quicker drying ａnd improved adhesion of the coating, pre-heating of the parts to about 80-120 °C before coating has proved to be effective.

Note

Stir well before use! Shelf-life: 18 month in closed original containers at room temperature.