White PTFE solid film lubricant

Performance Features

• Temperature range for use: -70/+140 °C; short term up to 250 °C
• forms a dry, firmly adhering lubricant film
• provides very good corrosion protection
• highly resistant to solvents, mineral oils ａnd synthetic fluids
• resistant to wear ａnd abrasion
• suitable for lifetime lubrication
• has good lubrication properties
• high load capacity
• produces surfaces with a decorative finish

Description

GLEITMO SFL 9560 is a white, heat-curing solid film lubricant having PTFE as a constituent for lubrication efficiency. The product forms a dry lubricating film, which is distinguished by its excellent lubricating effect, high degree of abrasion resistance ａnd very good corrosion protection. Because of its advanced binder system GLEITMO SFL 9560 can already be cured at 130 °C, thus protecting the substrate ａnd enabling energy to be saved. GLEITMO SFL 9560 is resistant to mineral oils ａnd many chemicals.

Field of application

GLEITMO SFL 9560 is used for the lifetime lubrication of metallic materials subjected to medium ａnd high pressures or slow sliding speeds as well as emergency lubrication. Examples are the lubrication of adjusting mechanisms (spindles ａnd slide rails) or machine components requiring dry lubrication ａnd good corrosion protection.

Method of application

Coating is carried out by spraying or using the dipping or centrifugal dipping methods. Before this happens, the parts to be coated must be thoroughly degreased with a solvent. The surfaces must be dry when the coating is applied. To increase the adhesive strength, ａnd therefore the lifetime, pre-treatment of the surfaces is recommended by phosphatising or sand-blasting. In order to achieve quicker drying ａnd improved adhesion of the coating, pre-heating of the parts to about 80-90 °C before coating has proved to be effective.

Notes

Stir well before use! Shelf-life: 12 month in closed original container at room temperature